Product name: Tantalum rod Tantalum alloy rod
Brand number: RO5200,R05400,TA1,TA2
Standard: ASTM B365
Purity: ≥99.95%
Process: cold rolling, pickling, shearing.
Technical conditions: in accordance with GB /T14841-93, ASTM B365-92
Specifications: According to customer requirements processing
Application: Used to make heating parts and heat insulation parts for vacuum blast furnace. In chemical industry, it can be used to make digester, heater, cooler, all kinds of utensils, etc., and it is widely used in aviation, aerospace industry, medical instruments and other fields.
Chemical composition:
brand Grade | Chemical composition %,Not more than Chemical composition, Max | |||||||||||
Fe | Si | Ni | W | Mo | Ti | Nb | O | C | H | N | Ta | |
Ta1 | 0.005 | 0.005 | 0.005 | 0.005 | 0.002 | 0.002 | 0.005 | 0.02 | 0.004 | 0.002 | 0.005 | allowance |
Ta2 | 0.005 | 0.005 | 0.005 | 0.005 | 0.002 | 0.002 | 0.1 | 0.03 | 0.1 | 0.002 | 0.01 | allowance |
Dimensional tolerance (mm)
diameter Diameter | Dia tolerance | Length | Tolerance | ||
Forging bar | drawbar | rod | |||
3.0-4.5 | - | 0.05 | - | 500-1500 | ±2 |
4.5-6.5 | ±0.15 | - | - | 500-1500 | ±2 |
6.5-10 | ±0.15 | - | - | 400-1500 | ±2 |
10-16 | ±0.15 | - | - | 300-1200 | ±2 |
16-18 | ±0.15 | - | - | 200-1500 | ±2 |
18-25 | - | - | ±0.5 | ±2 | |
25-40 | - | - | ±0.5 | ±2 | |
40-50 | - | - | ±0.6 | ±2 | |
50-65 | - | - | ±0.7 | ±2 |
Mechanical properties (annealed)
Bar, 0.125 in (3.18 mm) to 2.5" (63.5 mm) diameter | |||
brand | Minimum ultimate tensile strength, Lb/inch 2 (mpa) | The yield strength is minimal, Lb/inch 2 (mpa) | Elongation, minimum % (1 inch scale) |
RO5200/RO5400 | 25000 (172) | 15000 (103) | 25 |
RO5252 | 40000 (276) | 28000 (193) | 20 |
RO5255 | 70000 (482) | 55000 (379) | 20 |
RO5240 | 40000 (276) | 28000 (193) | 25 |
1. Tantalum has good resistance to chemical corrosion, and its corrosion rate in the chemical environment is 0~0.05mm/ a. In sulfuric acid, nitric acid, hydrochloric acid, aqua roya, perchloric acid, chloride, bromide, ammonia-ausic acid, phosphoric acid, chlorine oxides, hypochlorous acid, organic acid (including chloroacetic acid), hydrogen peroxide and all salts that do not produce free hydrofluoric acid or strong base in the hydrolysis reaction and in hot and cold seawater, have very good corrosion resistance. 2. But it has good temperature resistance, its melting point is 2996"℃, and has good heat conductivity.
3. Excellent cold forging, easy to work at significantly below room temperature, recrystallization temperature between 900℃ and 1450℃.
4. It has good biological adaptability and good compatibility with human body fluids. It will not cause anaphylaxis during medical operation.