Tantalum wire
Brand: Ta1, Ta2, TaW2.5, TaW7.5, TaW10, TaNb3, TaNb20, TaNb40, etc.
Standard: GB/T3463-1995;
Purity: purity of pure tantalum is greater than 99.95%;
State: Annealed state (M) or hard state (Y);
Size: Coil wire: Φ0.6~Φ5mm
Straight wire: Φ1.~Φ3*L2m(Max),
Capacitor grade tantalum wire is mainly used to make anode leads of tantalum electrolytic capacitors. The tantalum wire of capacitor grade produced by our company can be divided into more than 30 varieties according to different states and specifications. The smallest tantalum wire is Φ0.10mm. Tantalum wire is the key material for making tantalum capacitors. Tantalum capacitors are the best capacitors. About 65% of the world's tantalum is used in this field.
Chemical composition:
Chemical composition, Max | |||||||||||
Grade | C | N | O | H | Fe | Si | Ti | Ni | Nb | W | Mo |
Ta1 | 0.01 | 0.01 | 0.015 | 0.0015 | 0.005 | 0.005 | 0.002 | 0.002 | 0.003 | 0.01 | 0.01 |
Ta2 | 0.01 | 0.01 | 0.02 | 0.0015 | 0.03 | 0.02 | 0.005 | 0.005 | 0.1 | 0.04 | 0.04 |
Diameter and Tolerance:
(mm) Diameter | Ø0.10~Ø0.15 | Ø0.15~Ø0.30 | Ø0.30~Ø0.10 |
Tolerance | ±0.006 | ±0.007 | ±0.008 |
Ovality | 0.004 | 0.005 | 0.006 |
Mechanical properties
State | (MPa) | elongation(%) |
Mild (M) | 300-750 | 10-30 |
Semihard(Y2) | 750-1250 | 1-6 |
Hard(Y) | >1250 | 1-5 |
Number of bending times of oxygen brittleness resistance
Grade | Diameter (mm) | bending Times |
Ta1 | 0.10~0.40 | 3 |
>0.40 | 4 | |
Ta2 | 0.10~0.40 | 4 |
>0.40 | 6 |
1. Tantalum has good resistance to chemical corrosion, and its corrosion rate in the chemical environment is 0~0.05mm/ a. In sulfuric acid, nitric acid, hydrochloric acid, aqua roya, perchloric acid, chloride, bromide, ammonia-ausic acid, phosphoric acid, chlorine oxides, hypochlorous acid, organic acid (including chloroacetic acid), hydrogen peroxide and all salts that do not produce free hydrofluoric acid or strong base in the hydrolysis reaction and in hot and cold seawater, have very good corrosion resistance. 2. But it has good temperature resistance, its melting point is 2996"℃, and has good heat conductivity.
3. Excellent cold forging, easy to work at significantly below room temperature, recrystallization temperature between 900℃ and 1450℃.
4. It has good biological adaptability and good compatibility with human body fluids. It will not cause anaphylaxis during medical operation.